The effect of dwell on thermomechanical fatigue in superaustenitic steel Sanicro 25
  • Roman Petras,
  • Ivo Šulák,
  • Jaroslav Polak
Roman Petras
Institute of Physics of Materials Czech Academy of Sciences

Corresponding Author:petras@ipm.cz

Author Profile
Ivo Šulák
Institute of Physics of Materials Czech Academy of Sciences
Author Profile
Jaroslav Polak
Institute of Physics of Materials Czech Academy of Sciences
Author Profile


Superaustenitic steel Sanicro 25 has been subjected to in-phase and out-of-phase thermomechanical fatigue cycles in the temperature range from 250°C to 700°C. Both constant strain rate cycling and cycling with 10 minutes dwell at peak temperature were applied. The effect of the dwells on the cyclic response, internal structure and damage mechanism was studied. Cyclic hardening/softening curves, cyclic stress-strain curves and fatigue life curves were evaluated. The transmission electron microscopy was used to find modifications of the internal structure and precipitation of the nanoparticles. 10 min dwell at maximum temperature modified substantially the dislocation arrangement. Various nanoparticles representing the obstacles for dislocation motion were analysed and identified by energy dispersive X-ray spectroscopy in scanning transmission electron microscope. The damage mechanism operating under specific loading conditions was investigated on the surface as well as in the interior of the cycled specimens. Scanning electron microscopy combined with focused ion beam and electron backscatter diffraction was adopted to reveal the respective mechanisms responsible for crack nucleation and propagation. Effect of dwells on fatigue behaviour, modification of internal structure and damage mechanisms are analysed and discussed.
03 Aug 2020Submitted to Fatigue & Fracture of Engineering Materials & Structures
03 Aug 2020Submission Checks Completed
03 Aug 2020Assigned to Editor
04 Aug 2020Reviewer(s) Assigned
27 Aug 2020Review(s) Completed, Editorial Evaluation Pending
20 Sep 2020Editorial Decision: Revise Major
12 Oct 20201st Revision Received
12 Oct 2020Submission Checks Completed
12 Oct 2020Assigned to Editor
12 Oct 2020Reviewer(s) Assigned
27 Oct 2020Review(s) Completed, Editorial Evaluation Pending
02 Nov 2020Editorial Decision: Accept